1.0039 (S235JRH)

Classification

Country	Section	Category
Country	Section	Category
Germany	Non-alloy Steels	Base Steels

Chemical composition

Standard	Fe, %	Mn, %	P, %	C, %	S, %	N, %
Standard	Fe, %	Mn, %	P, %	C, %	S, %	N, %
DIN EN 10210-1:2006	> 98.311	< 1.4	< 0.04	< 0.2	< 0.04	< 0.009

Information on suppliers

Wish to advertise here?

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{Y}$ , $MPa$	$\epsilon_L$ , %	$KV_{L}$ , $J$	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{Y}$ , $MPa$	$\epsilon_L$ , %	$KV_{L}$ , $J$	Treatment
		< 3			360–510			27
		3–100			360–510
		100–120			350–500	195	22
		< 16				235
		16–40				225
		40–63				215	25
		63–80				215
		80–100				215
		< 40					26
		63–100					24

Properties

Property
Property
According to EN 10210-1 Thickness: < 3 mm ; yield strength: > 235 MPa
According to EN 10210-1 Thickness: < 3 mm ; tensile strength: 360 - 510 MPa
According to EN 10210-1 Thickness: 3 - 16 mm ; yield strength: > 235 MPa
According to EN 10210-1 Thickness: 3 - 16 mm ; yield strength: 360 - 510 MPa
According to EN 10210-1 Thickness: 16 - 40 mm ; yield strength: > 225 MPa
According to EN 10210-1 Thickness: 16 - 40 mm ; yield strength: 360 - 510 MPa
According to EN 10210-1 Thickness: 40 - 63 mm ; yield strength: > 215 MPa
According to EN 10210-1 Thickness: 40 - 63 mm ; yield strength: 360 - 510 MPa
According to EN 10210-1 Thickness: 63 - 80 mm ; yield strength: > 215 MPa
According to EN 10210-1 Thickness: 63 - 80 mm ; tensile strength: 360 - 510 MPa
According to EN 10210-1 Thickness: 80 - 100 mm ; yield strength: > 215 MPa
According to EN 10210-1 Thickness: 80 - 100 mm ; yield strength: 360 - 510 MPa
According to EN 10210-1 Thickness: 100 - 120 mm ; yield strength: > 195 MPa
According to EN 10210-1 Thickness: 100 - 120 mm ; tensile strength: 350 - 500 MPa
According to EN 10210-1 Longitudinal samples Thickness: < 40 mm ; elongation: > 26 %
According to EN 10210-1 Longitudinal samples Thickness: 40 - 63 mm ; elongation: > 25 %
According to EN 10210-1 Longitudinal samples Thickness: 63 - 100 mm ; elongation: > 24 %
According to EN 10210-1 Longitudinal samples Thickness: 100 - 120mm ; elongation: > 22 %
According to EN 10210-1 Transverse specimens Thickness: < 40 mm ; elongation: > 24 %
According to EN 10210-1 Transverse specimens Thickness: 40 - 63 mm ; elongation: > 23 %
According to EN 10210-1 Transverse specimens Thickness: 63 - 100 mm ; elongation: > 22 %
According to EN 10210-1 Transverse specimens Thickness: 100 - 120mm ; elongation: > 20 %
According to EN 10210-1 Test blow Job blow KV at 20°C [68°F]: > 27 j
Density: 7.85 g / cm3
Weldability According to ISO / TR 20172 Group: 1.1

Analogues

Germany	CIS, Russia, Ukraine	USA
Germany	CIS, Russia, Ukraine	USA
S 235 JRH	Ст3пс-е	260W

Standards

Standard	Description
Standard	Description
EN 10210-1
EN 10219-1
DIN EN 10210-1:2006
DIN EN 10210-3:2019
DIN EN 10219-1:2006
DIN EN 10219-3:2019

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Mn	%	Manganese
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur
N	%	Nitrogen

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma_{Y}$	$MPa$	Yield strength
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\epsilon_L$	%	Elongation at break (longitudinal)
$KV_{L}$	$J$	Impact energy (longitudinal)