1.4881 (X70CrMnNiN21-6)

Classification

Country	Section	Category
Country	Section	Category
Germany	Stainless and Heat Resisting Steels	Heat Resistant Steels with Ni > = 2.5%

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Ni, %	P, %	C, %	S, %	N, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Ni, %	P, %	C, %	S, %	N, %
	67.16–72.25	< 0.8	5.5–7	20–22	1.4–1.9	< 0.05	0.65–0.75	0.02–0.06	0.18–0.28

Information on suppliers

Wish to advertise here?

Physical characteristics

Temperature, °C	$$\alpha\cdot 10^{6}$$, $$K^{-1}$$	$$\varkappa$$, $$\frac{W}{m\cdot K}$$	$$\rho$$, $$\frac{kg}{m^3}$$
Temperature, °C	$$\alpha\cdot 10^{6}$$, $$K^{-1}$$	$$\varkappa$$, $$\frac{W}{m\cdot K}$$	$$\rho$$, $$\frac{kg}{m^3}$$
20		13	7700
100	17.1
300	18.1
500	19
700	20

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$$\sigma _{U}$$, $$MPa$$	$$\sigma_{0.2}$$, $$MPa$$	$$\epsilon_L$$, %	$$\psi$$, %	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$$\sigma _{U}$$, $$MPa$$	$$\sigma_{0.2}$$, $$MPa$$	$$\epsilon_L$$, %	$$\psi$$, %	Treatment
					980–1180	< 590	< 8	< 15	After treatment and aging

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Ni	%	Nickel
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur
N	%	Nitrogen

Description of physical characteristics

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$$\alpha\cdot 10^{6}$$	$$K^{-1}$$	Coefficient of thermal (linear) expansion (range 20°C–T)
$$\varkappa$$	$$\frac{W}{m\cdot K}$$	Coefficient of thermal conductivity (the heat capacity of the material)
$$\rho$$	$$\frac{kg}{m^3}$$	The density of the material

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$$\sigma_{0.2}$$	$$MPa$$	Tensile stress required to produce a total elongation of 0.2%
$$\sigma _{U}$$	$$MPa$$	Ultimate tensile strength
$$\epsilon_L$$	%	Elongation at break (longitudinal)
$$\psi$$	%	Reduction in cross section on fracture