1.4940 (X7CrNiTi18-10)

Classification

Country	Section	Category
Country	Section	Category
Germany	Stainless and Heat Resisting Steels	Materials with Elevated Temperature Properties

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Ti, %	Ni, %	P, %	C, %	S, %	N, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Ti, %	Ni, %	P, %	C, %	S, %	N, %
EEN 10088-1	63.965–73.76	< 1	< 2	17–19	0.2–0.8	9–13	< 0.04	0.04–0.08	< 0.015	< 0.1

Information on suppliers

Wish to advertise here?

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{0.2}$ , $MPa$	$\epsilon_L$ , %	$\epsilon_T$ , %	$KV_{L}$ , $J$	$KV_{T}$ , $J$	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{0.2}$ , $MPa$	$\epsilon_L$ , %	$\epsilon_T$ , %	$KV_{L}$ , $J$	$KV_{T}$ , $J$	Treatment
				solution annealing	510–710	190	35	30	100	60

Standards

Standard	Description
Standard	Description
EEN 10088-1

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Ti	%	Titan
Ni	%	Nickel
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur
N	%	Nitrogen

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma_{0.2}$	$MPa$	Tensile stress required to produce a total elongation of 0.2%
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\epsilon_L$	%	Elongation at break (longitudinal)
$\epsilon_T$	%	Elongation at break (transverse)
$KV_{L}$	$J$	Impact energy (longitudinal)
$KV_{T}$	$J$	Impact energy (transverse)