28C

Weldability without restrictions.

manufacturing valves periodic profile classes At600S (Al-IVc) At800 (At-the V), designed for reinforcement of concrete structures

Classification

Country Section Category
CIS, Russia, Ukraine Structural steel Low alloy structural steel for welded structures

Chemical composition

Standard Fe, % Si, % Mn, % Cu, % As, % P, % C, % S, %
GOST 10884-94 97.115–98.25 0.9–1.2 0.6–0.9 < 0.3 < 0.08 < 0.04 0.25–0.32 < 0.045

Information on suppliers

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers \sigma _{U}, MPa \sigma_{P}, MPa \epsilon_L, % Treatment
Fittings GOST 10884-71 Ø 16–32 980 785 7

Technological Properties

Weldability
no limits

Analogues

Germany
BSt 420 S

Standards

Standard Description
GOST 10884-94

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cu % Copper
As % Arsenic
P % Phosphorus
C % Carbon
S % Sulfur

Description of mechanical properties

Parameter Units of measurement Description
\sigma _{U} MPa Ultimate tensile strength
\sigma_{P} MPa Proportionality limit
\epsilon_L % Elongation at break (longitudinal)

Designation of types of weldability

Parameter Units of measurement Description
no limits Welding is performed without heating and without subsequent heat treatment
Boundedly welded Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures