AM5 (AL19)
for the production of shaped castings; alloy high-strength heat-resistant
for the production of shaped castings; alloy high-strength heat-resistant
| Standard | Fe, % | Si, % | Mg, % | Mn, % | Ti, % | Cu, % | Zn, % | Ni, % | Zr, % | Al, % |
|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Fe, % | Si, % | Mg, % | Mn, % | Ti, % | Cu, % | Zn, % | Ni, % | Zr, % | Al, % |
| GOST 1583-93 | < 0.2 | < 0.3 | < 0.05 | 0.6–1 | 0.15–0.35 | 4.5–5.3 | < 0.2 | < 0.1 | < 0.2 | 92.3–94.75 |
| Temperature, °C | $$E\cdot 10^{9}$$, $$MPa$$ | $$\alpha\cdot 10^{6}$$, $$K^{-1}$$ | $$\varkappa$$, $$\frac{W}{m\cdot K}$$ | $$\rho$$, $$\frac{kg}{m^3}$$ | $$c\cdot 10^{-3}$$, $$\frac{J}{kg\cdot K}$$ | $$R\cdot 10^{-6}$$, $$\Omega\cdot m$$ |
|---|---|---|---|---|---|---|
| Temperature, °C | $$E\cdot 10^{9}$$, $$MPa$$ | $$\alpha\cdot 10^{6}$$, $$K^{-1}$$ | $$\varkappa$$, $$\frac{W}{m\cdot K}$$ | $$\rho$$, $$\frac{kg}{m^3}$$ | $$c\cdot 10^{-3}$$, $$\frac{J}{kg\cdot K}$$ | $$R\cdot 10^{-6}$$, $$\Omega\cdot m$$ |
| 20 | 0.7 | 2780 | 59.5 | |||
| 100 | 19.5 | 130 | 838 |
| Rolling | Standard | Size, mm | Tension | Classifiers | $$\sigma _{U}$$, $$MPa$$ | d5, % | Treatment |
|---|---|---|---|---|---|---|---|
| Rolling | Standard | Size, mm | Tension | Classifiers | $$\sigma _{U}$$, $$MPa$$ | d5, % | Treatment |
| Castings | GOST 1583-93 | 294–333 | 2–8 |
| Rolling | Standard | Classifiers | Value, HBW |
|---|---|---|---|
| Rolling | Standard | Classifiers | Value, HBW |
| Castings | GOST 1583-93 | 70–90 |
| Standard | Description |
|---|---|
| Standard | Description |
| GOST 1583-93 | |
| GOST Р 55375-2012 | |
| DSTU 2839-94 |
| Parameter | Units of measurement | Description |
|---|---|---|
| Parameter | Units of measurement | Description |
| $$E\cdot 10^{9}$$ | $$MPa$$ | Elastic modulus |
| $$\alpha\cdot 10^{6}$$ | $$K^{-1}$$ | Coefficient of thermal (linear) expansion (range 20°C–T) |
| $$\varkappa$$ | $$\frac{W}{m\cdot K}$$ | Coefficient of thermal conductivity (the heat capacity of the material) |
| $$\rho$$ | $$\frac{kg}{m^3}$$ | The density of the material |
| $$c\cdot 10^{-3}$$ | $$\frac{J}{kg\cdot K}$$ | The specific heat of the material (range 20°C–T) |
| $$R\cdot 10^{-6}$$ | $$\Omega\cdot m$$ | Electrical resistivity |