AMg3 (1530)

For the manufacture of semifinished products by hot or cold deformation; corrosion resistance high

Classification

Country	Section	Category
Country	Section	Category
CIS, Russia, Ukraine	Aluminum, aluminum alloys	Wrought Aluminum Alloys

Chemical composition

Standard	Fe, %	Si, %	Mg, %	Mn, %	Cr, %	Ti, %	Cu, %	Zn, %	Al, %
Standard	Fe, %	Si, %	Mg, %	Mn, %	Cr, %	Ti, %	Cu, %	Zn, %	Al, %
GOST 4784-97	< 0.5	0.5–0.8	3.2–3.8	0.3–0.6	< 0.05	< 0.1	< 0.1	< 0.2	93.8–96

Information on suppliers

Wish to advertise here?

Physical characteristics

Temperature, °C	$E\cdot 10^{9}$ , $MPa$	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\varkappa$ , $\frac{W}{m\cdot K}$	$\rho$ , $\frac{kg}{m^3}$	$c\cdot 10^{-3}$ , $\frac{J}{kg\cdot K}$	$R\cdot 10^{-6}$ , $\Omega\cdot m$
Temperature, °C	$E\cdot 10^{9}$ , $MPa$	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\varkappa$ , $\frac{W}{m\cdot K}$	$\rho$ , $\frac{kg}{m^3}$	$c\cdot 10^{-3}$ , $\frac{J}{kg\cdot K}$	$R\cdot 10^{-6}$ , $\Omega\cdot m$
20	71			2660		0.0496
100		23.5	151		0.88

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\epsilon_L$ , %	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\epsilon_L$ , %	Treatment
Trumpet					180	70	15
Round	GOST 21488-97				175	80	13
Tape				annealing	185–195	80–100	15
Tape				cold-work, half-load	245	195	7
Profile					176	78	12
Sheet					165–185	59–69	11–12

Brinell hardness number

Rolling	Standard	Classifiers	Value, HBW
Rolling	Standard	Classifiers	Value, HBW
Alloy			45

Technological Properties

Weldability
Weldability
no limits

Analogues

Germany	USA
Germany	USA
3.3535	A95154

Standards

Standard	Description
Standard	Description
GOST 4784-97
GOST 18482-79
GOST 21631-76	GOST 21631-76
GOST 23697-1979
GOST 9498-79	GOST 9498 - 79

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mg	%	Magnesium
Mn	%	Manganese
Cr	%	Chrome
Ti	%	Titan
Cu	%	Copper
Zn	%	Zinc
Al	%	Aluminium

Description of physical characteristics

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$E\cdot 10^{9}$	$MPa$	Elastic modulus
$\alpha\cdot 10^{6}$	$K^{-1}$	Coefficient of thermal (linear) expansion (range 20°C–T)
$\varkappa$	$\frac{W}{m\cdot K}$	Coefficient of thermal conductivity (the heat capacity of the material)
$\rho$	$\frac{kg}{m^3}$	The density of the material
$c\cdot 10^{-3}$	$\frac{J}{kg\cdot K}$	The specific heat of the material (range 20°C–T)
$R\cdot 10^{-6}$	$\Omega\cdot m$	Electrical resistivity

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\sigma_{P}$	$MPa$	Proportionality limit
$\epsilon_L$	%	Elongation at break (longitudinal)

Designation of types of weldability

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
no limits		Welding is performed without heating and without subsequent heat treatment
Boundedly welded		Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld		For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures