MNA13-3 (KunialA)

rods for the manufacture of products with increased strength in mechanical engineering

Classification

Country	Section	Category
Country	Section	Category
CIS, Russia, Ukraine	Copper, copper alloys	Copper-Nickel Alloys

Chemical composition

Standard	Fe, %	Mn, %	Cu, %	Al, %	Pb, %	Ni + Co, %
Standard	Fe, %	Mn, %	Cu, %	Al, %	Pb, %	Ni + Co, %
GOST 492-2006	< 1	< 0.5	80.1–85.7	2.3–3	< 0.002	12–15

Information on suppliers

Wish to advertise here?

Physical characteristics

Temperature, °C	$\rho$ , $\frac{kg}{m^3}$
Temperature, °C	$\rho$ , $\frac{kg}{m^3}$
20	8500

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\epsilon_L$ , %	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\epsilon_L$ , %	Treatment
The alloy is soft					380–470	10–15
Alloy hard					900–950	2–4

Brinell hardness number

Rolling	Standard	Classifiers	Value, HBW
Rolling	Standard	Classifiers	Value, HBW
Alloy hard			255

Casting and technological parameters

melting point, °C	Hot working temperature, °C
melting point, °C	Hot working temperature, °C
1120	900–1000

Analogues

USA
USA
C72400

Standards

Standard	Description
Standard	Description
GOST 492-2006
GOST 492-1973
DSTU GOST 492:2007

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Mn	%	Manganese
Cu	%	Copper
Al	%	Aluminium
Pb	%	Lead
Ni + Co	%	Nickel + Cobalt

Description of physical characteristics

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\rho$	$\frac{kg}{m^3}$	The density of the material

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\epsilon_L$	%	Elongation at break (longitudinal)

Description of the casting and technological parameters

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
melting point	°C	The temperature at which solid crystalline body makes the transition to the liquid state and Vice versa
Hot working temperature	°C	The temperature at which the plastic-deformed metal recrystallizes during the pressure treatment