Iron-cobalt-nickel alloy precision 24NK

No foreign analogues

It is intended for connection with ceramics like «22XC» and «polycor», leucosapphire, etc. high-temperature solders with a melting point of 800−1000 ° C

Classification

Country	Section	Category
Country	Section	Category
CIS, Russia, Ukraine	Heat resistant steels and alloys	Heat resistant alloys

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Co, %	Ni, %	C, %
Standard	Fe, %	Si, %	Mn, %	Co, %	Ni, %	C, %
GOST 10994-74	45.8–48.5	< 0.3	< 0.35	27.5–28.5	24–25	< 0.05

Information on suppliers

Wish to advertise here?

Physical characteristics

Temperature, °C	$E\cdot 10^{9}$ , $MPa$	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\rho$ , $\frac{kg}{m^3}$	$R\cdot 10^{-6}$ , $\Omega\cdot m$
Temperature, °C	$E\cdot 10^{9}$ , $MPa$	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\rho$ , $\frac{kg}{m^3}$	$R\cdot 10^{-6}$ , $\Omega\cdot m$
20	144	5.5–8	8400	500

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{Y}$ , $MPa$	d5, %	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{Y}$ , $MPa$	d5, %	Treatment
Tape	GOST 14086-68	<2.0	Transverse	raw, cold rolling, thin, Transverse	480–500	270–290	23

Casting and technological parameters

melting point, °C
melting point, °C
1450

Technological Properties

Weldability	Flake Susceptibility	Propensity to temper brittleness
Weldability	Flake Susceptibility	Propensity to temper brittleness
no limits	not sensitive	loathsome

Limit operating modes

Standard	Температура, °C
Standard	Температура, °C
GOST 10994-74	< 420

Standards

Standard	Description
Standard	Description
GOST 10994-74

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Co	%	Cobalt
Ni	%	Nickel
C	%	Carbon

Description of physical characteristics

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$E\cdot 10^{9}$	$MPa$	Elastic modulus
$\alpha\cdot 10^{6}$	$K^{-1}$	Coefficient of thermal (linear) expansion (range 20°C–T)
$\rho$	$\frac{kg}{m^3}$	The density of the material
$R\cdot 10^{-6}$	$\Omega\cdot m$	Electrical resistivity

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
d5	%	Elongation at break
$\sigma_{Y}$	$MPa$	Yield strength
$\sigma _{U}$	$MPa$	Ultimate tensile strength

Description of the casting and technological parameters

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
melting point	°C	The temperature at which solid crystalline body makes the transition to the liquid state and Vice versa

Designation of types of weldability

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
no limits		Welding is performed without heating and without subsequent heat treatment
Boundedly welded		Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld		For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures