EP605

Classification

Country	Section	Category
Country	Section	Category
CIS, Russia, Ukraine	Heat resistant steels and alloys	Heat resistant alloys

Information on suppliers

Wish to advertise here?

Physical characteristics

Temperature, °C	$E\cdot 10^{9}$ , $MPa$	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\varkappa$ , $\frac{W}{m\cdot K}$	Cp, Дж/кг·К
Temperature, °C	$E\cdot 10^{9}$ , $MPa$	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\varkappa$ , $\frac{W}{m\cdot K}$	Cp, Дж/кг·К
20	200	9.7	30.2	470

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{Y}$ , $MPa$	d5, %	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{Y}$ , $MPa$	d5, %	Treatment
Trumpet	TU 14-1-1019-74	400	Transverse		450–600	300–400	20–25

Brinell hardness number

Rolling	Standard	Classifiers	Value, HBW
Rolling	Standard	Classifiers	Value, HBW
Trumpet	TU 14-1-1019-74		190–220

Technological Properties

Weldability	Flake Susceptibility	Propensity to temper brittleness
Weldability	Flake Susceptibility	Propensity to temper brittleness
Difficult to weld	insensitive	inclined

Heat Treatment Modes

Treatment
Treatment
Tempering, vacation

Description of physical characteristics

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
Cp	Дж/кг·К	Specific heat of material
$E\cdot 10^{9}$	$MPa$	Elastic modulus
$\alpha\cdot 10^{6}$	$K^{-1}$	Coefficient of thermal (linear) expansion (range 20°C–T)
$\varkappa$	$\frac{W}{m\cdot K}$	Coefficient of thermal conductivity (the heat capacity of the material)

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
d5	%	Elongation at break
$\sigma_{Y}$	$MPa$	Yield strength
$\sigma _{U}$	$MPa$	Ultimate tensile strength

Designation of types of weldability

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
no limits		Welding is performed without heating and without subsequent heat treatment
Boundedly welded		Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld		For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures