VT5-1

Hardness VT5−1 HB 10 ^-1 = 241 — 321 MPa. Weldability without restrictions.

Stamped parts and components operating at temperatures up to 450 ° C; good corrosion resistance; α class structure

Classification

Country	Section	Category
Country	Section	Category
CIS, Russia, Ukraine	Titanium, titanium alloys	Wrought Titanium Alloys

Chemical composition

Standard	Fe, %	Si, %	Sn, %	Ti, %	V, %	Zr, %	Al, %	C, %	O, %	N, %	H, %
Standard	Fe, %	Si, %	Sn, %	Ti, %	V, %	Zr, %	Al, %	C, %	O, %	N, %	H, %
GOST 19807-91	< 0.3	< 0.12	2–3	88.83–93.4	< 1	< 0.3	4.3–6	< 0.1	< 0.15	< 0.05	< 0.015

Information on suppliers

Wish to advertise here?

Physical characteristics

Temperature, °C	$E\cdot 10^{9}$ , $MPa$	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\varkappa$ , $\frac{W}{m\cdot K}$	$\rho$ , $\frac{kg}{m^3}$	$c\cdot 10^{-3}$ , $\frac{J}{kg\cdot K}$	$R\cdot 10^{-6}$ , $\Omega\cdot m$
Temperature, °C	$E\cdot 10^{9}$ , $MPa$	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\varkappa$ , $\frac{W}{m\cdot K}$	$\rho$ , $\frac{kg}{m^3}$	$c\cdot 10^{-3}$ , $\frac{J}{kg\cdot K}$	$R\cdot 10^{-6}$ , $\Omega\cdot m$
20	110			4425	0.502	1.38
100		8.3			0.544
200		9.3	10.88		0.565
300		9.7	12.14		0.586
400		10	13.14		0.628
500		10.3	14.65		0.67
600		10.4	15.91

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	$KCU\cdot 10^{3}$ , $\frac{J}{m^2}$	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	$KCU\cdot 10^{3}$ , $\frac{J}{m^2}$	Treatment
Sheet	GOST 22178-76			annealing	735	8–15
Round	GOST 26492-85			annealing	745–785	6–8	15–20	400
Round	GOST 26492-85			enhanced quality	745–980	6–10	18–25	400–450
Plate	GOST 23755-79	11–35			735–930	6	12

Brinell hardness number

Rolling	Standard	Classifiers	Value, HBW
Rolling	Standard	Classifiers	Value, HBW
			241–321

Technological Properties

Weldability
Weldability
no limits

Analogues

Germany	USA
Germany	USA
3.7114	5Al-2.5Sn
3.7115	Grade6

Standards

Standard	Description
Standard	Description
GOST 19807-91

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Sn	%	Tin
Ti	%	Titan
V	%	Vanadium
Zr	%	Zirconium
Al	%	Aluminium
C	%	Carbon
O	%	Oxygen
N	%	Nitrogen
H	%	Hydrogen

Description of physical characteristics

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$E\cdot 10^{9}$	$MPa$	Elastic modulus
$\alpha\cdot 10^{6}$	$K^{-1}$	Coefficient of thermal (linear) expansion (range 20°C–T)
$\varkappa$	$\frac{W}{m\cdot K}$	Coefficient of thermal conductivity (the heat capacity of the material)
$\rho$	$\frac{kg}{m^3}$	The density of the material
$c\cdot 10^{-3}$	$\frac{J}{kg\cdot K}$	The specific heat of the material (range 20°C–T)
$R\cdot 10^{-6}$	$\Omega\cdot m$	Electrical resistivity

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\epsilon_L$	%	Elongation at break (longitudinal)
$\psi$	%	Reduction in cross section on fracture
$KCU\cdot 10^{3}$	$\frac{J}{m^2}$	Impact toughness

Designation of types of weldability

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
no limits		Welding is performed without heating and without subsequent heat treatment
Boundedly welded		Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld		For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures